Optical damage resistant ridge waveguides for blue and near UV wavelengths have been fabricated using high-temperature Zr and Zn diffusion doping and vapor transport equilibration (VTE) of congruent LiTaO_3 crystals. For both dopants high optical damage thresholds >10 MW/cm^2 for 532 nm light were demonstrated at room temperature, which can be increased by a factor ~3 when heating the samples to ~150°C. Ridge waveguides with low optical losses of ~0.4 dB/cm were fabricated using diamond-blade dicing. First-order periodic poling with grating periods of ~3 μm can be used for efficient nonlinear frequency conversion for both SHG (800 nm pump) or SPDC (400 nm pump) processes.